| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 比重 | ASTM D1505 | 1.40 | g/cm3 | |
| 熔体质量流动速率 | 343℃, 2.16KG | ASTM D1238 | 6.5 | g/10min | |
| 成型收缩率 | ASTM D955 | 0.3 | % | ||
| 机械性能 | 拉伸强度 | ASTM D638 | 97 | MPa | |
| 拉伸伸长率 | ASTM D638 | 3 | % | ||
| 拉伸模量 | ASTM D638 | 6000 | MPa | ||
| 弯曲强度 | ASTM D790 | 148 | MPa | ||
| 弯曲模量 | ASTM D790 | 5500 | MPa | ||
| IZOD缺口冲击强度 | ASTM D256 | 5.3 | KJ/m2 | ||
| 拉伸冲击强度 | ASTM D1822 | 110 | KJ/m2 | ||
| 电气性能 | 绝缘强度 | ASTM D149 | 19 | kV/mm | |
| 体积电阻 | ASTM D257 | 2×1016 | Ω·cm | ||
| 介电常数 | 60 Hz | ASTM D150 | 3.31 | ||
| 介电常数 | 1000000 Hz | ASTM D150 | 3.28 | ||
| 介质损耗因数 | 60 Hz | ASTM D150 | 0.0008 | ||
| 介质损耗因数 | 1000000 Hz | ASTM D150 | 0.0060 | ||
| 热性能 | 热变形温度 | 1.82MPa | ASTM D648 | 180 | ℃ |
| 阻燃性 | 3.2 mm | UL94 | HB | 级 | |